PENGARUH PARAMETER PROSES TERHADAP KUAT TARIK SPESIMEN UJI ASTM D638 TYPE IV MENGGUNAKAN FILAMEN ESUN PLA+
Keywords:
3D Printing, FDM, Esun PLA Filament, Tensile Strength, TaguchiAbstract
FDM is one of the most frequently used methods in 3D Printing technology that is used to print filament products as material because this technique is easy to print 3D at a relatively low cost. Many researches on tensile testing have been carried out using PLA and ABS filaments, while for Esun PLA+ filaments are still rarely done. From these problems, it is necessary to research to get the effect of layer thickness and nozzle temperature to get the highest tensile strength value using Esub PLA+ filament. This research uses the Taguchi L25 OA method on the Anet 8 plus pro 3D Printing machine with dimensions of XYZ 300mm x 300mm x 350mm using a nozzle measuring 0.4 mm and using Esun PLA+ filament with a diameter of 1.75 mm. The process parameters in this research are Printing speed, nozzle temperature, layer thickness, cooling speed and orientation. The shape of the test specimen is in accordance with the ASTM d638 type IV standard. while to design the process parameters using L25 OA. Based on the results of this study, the highest tensile strength value with layer thickness (0.10mm) and nozzle temperature (2150C).
Downloads
References
Yolanda , Djami, S., & Lubis, S. (2016). PENGARUH ORIENTASI OBJEK PADA PROSES 3D PRINTING BAHAN POLYMER PLA DAN ABS TERHADAP KEKUATAN TARIK DAN KETELITIAN DIMENSI PRODUK. SINERGI Vol. 20, No. 1, Februari 2016, 1-9.
Andriyansyah, D., Herianto, & Purfaji. (2018). OPTIMASI PARAMETER PROSES 3D PRINTING TERHADAP KUAT TARIK FILAMEN POLYLACTIC ACID MENGGUNAKAN METODE TAGUCHI. Departemen Teknik Mesin dan Industri Fakultas Teknik Universitas Gadjah Mada Yogyakarta Jl. Grafika No. 2 Yogyakarta 55281 Indonesia , 8.
Kholil, A., Aufi, F., & Syaefudin, E. A. (2020). Pengaruh layer thickness dan orientasi 3D Printing terhadap uji tarik material ABS. NCIET, 1-8.
Lubis, S., & Sutanto, D. (2016). PENGARUH POSISI ORIENTASI OBJEK PADA PROSES RAPID PROTOTYPING 3D PRINTING TERHADAP KEKUATAN TARIK MATERIAL POLYMER. SINERGI Vol.20, No.3, Oktober 2016: 229-238, 1-10.
Pristiansyah, Hasdiansah, & Sugiyarto. (2019). Optimasi Parameter Proses 3D Printing FDM Terhadap Akurasi Dimensi Menggunakan Filament Eflex . Vol. 11 No. 01 (2019) , 1-8.
Soejanto, I. (2009). Desain Eksperimen dengan Metode Taguchi. Yogjakarta; Graha Ilmu.
Suzen, Z. S., Hasdiansah, & Yulianto. (2020). Pengaruh Tipe Infil Dan Temperature Nozzle Terhadap Kekuatan Tarik Produk 3D Printing Filamen Pla + Esun. Manutech, 1-8.
Yudha Bika Pratama, Hasdiansah, & Pristiansyah. (2021). Pengaruh Parameter Proses Slicing Software Terhadap Kekasaran Permukaan Printing Part Filamen ST-PLA. Manutech, 8.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2021 Wahyudi Hafizi Pratama, Hasdiansah Hasdiansah
This work is licensed under a Creative Commons Attribution-NonCommercial-ShareAlike 4.0 International License.